ASTM B829 / ASME SB829 Nickel and Nickel Alloys Seamless Pipe and Tube supplier & distributor in India
ASTM B-829 / ASME SB-829
SPECIFICATION FOR GENERAL REQUIREMENTS FOR NICKEL AND NICKEL ALLOYS SEAMELSS PIPE AND TUBE
1.Scope
1.1 This specification contains various reuiremens that, with the exception of Sections 5 and 10 are mandatory requiremants to the following ASTM nickel and nickel alloy, seamless pipe and tube specification.
1.2 One or more of the test requirements of Section 5 apply only if specifically stated in the product specification or in the purchase oder.
1.3 In case of conflict between a requirement of the product specification and requirement of this general specification, only the requirement of te product specification need to be satisfied.
1.4 The values ststed in inch-pound units are to be regarded as the standard. The values given in parentheses are for information only.
1.5 The following safety hazards caveat pertains only to the test method portion, Section 5, of this standard: This standard does not purport to address all of tne safety problems, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine tne applicability of regulatry limitations prior to use.
Ttile of Specification
ASTM Designation
Nickel Seamless Pipe and Tube
B 161
Seamless Nickel and Nickel Alloy, Condenser and Heat Exchanger Tubes
B 163
Nickel-Copper Alloy (UNS N04400) Seamless Pipe and Tubes
B 165
Nickel-Chromium-Iron Alloys (UNS N06600, N06601, and N06690) Seamless Pipe and Tube
B 167
Nickel-Iron-Chromium Alloy Seamless Pipe and Tube
B 407
Nickel-Iron-Chromium-Molybdenum-Copper Alloy (UNS N08825 and N08221) Seamless Pipe and Tube
B 423
Nickel-Chromium-Molybdenum-Columbium Alloys(UNS N06625) Pipe and Tube
B 444
Nickel-Chromium-Molybdenum-Columbium Alloys (UNS N06625) Pipe and Tube
B 445
Nickel-Iron-Chromium-Silicon Alloys (UNS N08330 and UNS N08332) Seamless Pipe
B 535
Copper-Beryllium Alloy Forgings and Extrusion
B 570
Seamless d Nickel and Nickel-Cobalt Alloy Pipe and Tube
B 622
UNS N08904 and UNS N08925 Seamless Pipe and Tube
B 677
UNS N08028 Seamless Tubes
B 668
Iron-Nickel-Chromium-Molybdenum Alloys (UNS N08366 and UNS N08367) Seamless Pipe and Tube
B 690
Ni-Cr-Mo-Co-W-Fe-Si Alloy (UNS N06333) Seamless Pipe and Tube
B 722
Seamless UNS N08020, UNS N08026, and UNS N08024 Nickel-Alloy Pipe and Tube
B 729
Chemical Composition
In case of disagreement, the chemical composition shall be determined in accordance with the following method:
UNS No. Prefixes
ASTM MEthod
N02
E 39
N04
E76
N06, N08
E354 E350A
AMethods E 350 are to be used for elements not covered by Test Method E 354.
TALBLE1 PRODUCT (CHECK) ANALYSIS TOLERANCE
Element
Specified Limit(min or max), %
Tolerance under min or over max of Specified Element, %
Nickel
Over 10.00 to 20.00, incl
0.20
Over 20.00 to 30.00, incl
0.25
Over 30.00 to 40.00, incl
0.30
Over 40.00 to 60.00, incl
0.35
Over 60.00 to 90.00, incl
0.45
Over 90.00
0.60
Chromium
Up to 1.00, incl
0.05
Over 5.00 to 15.00, incl
0.15
Over 15.00 to 25.00, incl
0.25
Over 25.00 to 35.00, incl
0.30
Molybdenum
Up to 1.00, incl
0.03
Over 1.00 to 3.00, incl
0.05
Over 3.00 to 5.00, incl
0.10
Over 5.00 to 20.00, incl
0.15
Iron
Up to 0.50, incl
0.03
Over 0.50 to 2.50, incl
0.05
Over 2.50 to 5.00, incl
0.07
Over 5.00 to 10.00, incl
0.010
Over 10.00 to 15.00, incl
0.15
Over 15.00 to 30.00, incl
0.30
Over 30.00 to 40.00, incl
0.45
Tungsten
Up to 1.00, incl
0.04
Over 1.00 to 3.00, incl
0.10
Over 3.00 to 5.00, incl
0.15
Carbon
Up to 0.02, incl
0.005
Over 0.02 to 0.20, incl
0.001
Over 0.20 to 0.60, incl
0.02
Silicon
Over 0.05 to 0.25, incl
0.02
Over 0.25 to 0.50, incl
0.03
Over 0.50 to 1.00, incl
0.05
Over 1.00 to 2.00, incl
0.10
Cobalt
Over 0.20 to 1.00, incl
0.03
Over 1.00 to 5.00, incl
0.05
Over 15.00 to 20.00, incl
0.20
Over 20.00 to 25.00, incl
0.25
Manganese
Up to 1.00, incl
0.03
Over 1.00 t 3.00, incl
0.04
Vanadium
Up to 0.50, incl
0.04
Phosphorus
All
0.005
Sulfur
Up to 0.02, incl
0.003
Over 0.02 to 0.06, incl
0.005
Titanium
Up to 0.10, incl
0.02
Over 0.10 to 0.50, incl
0.03
Over 0.50 to 1.00, incl
0.04
Over 1.00 to 2.00, incl
0.05
Copper
Up to 0.50, incl
0.03
Over 0.50 to 5.00, incl
0.04
Over 20.00 to 30.00, incl
0.15
Over 30.00 to 40.00, incl
0.20
Columbium+Tantalum
Up to 1.50, incl
0.05
Over 1.50 to 3.00, incl
0.10
Over 3.00 to 5.00, incl
0.15
Aluminum
Up to 0.10, incl
0.02
Over 0.10 to 0.50, incl
0.05
Over 0.50 to 2.00, incl
0.10
Boron
Up to 0.10, incl
0.002
Over 0.10 to 0.50, incl
0.00
Magnesium
Up to 0.05, incl
0.01
Zirconium
Up to 0.05, incl
0.01
Test
Rounded Unit for Observed or Calculated Value
Chemical composition and tolerances (when expressed in decimals)
Nearest unit in the last right-hand place of figures of the specified limit. If two choces are possible, as when the digits dropped are exactly a 5 or a 5 followed only by zeros, choose the one ending in an even digit, with zero defined as an even digit.
Tensile strength, and yield strength
Nearest 1000 psi (6.9 MPa)
Elongation
Nearest 1%
Grain size: 0.0024 in. (0.060 mm) or larger
Nearest multiple of 0.0002 in. (0.005mm)
Less than 0.0024 in.(0.060mm)
Nearest multiple of 0.0001 in. (0.002 mm)
TABLE2 DIMENSIONS OF PIPE
NOTE 1 - The following table is a reprint of Table 1 of ANSI B36.19. NOTE 2 - The decimal thicknesses listed for the respective pipe sizes represent their nominal wall dimensions.
ASchedules 5S and 10S wall thicknesses do not permit threading in accordance with ANSI B1.20.1. BThese do not conform to ANSI B36.10.
TABLE3 PERMISSIBLE VARIATIONS FOR OUTSIDE DIAMETE R AND WALL THICKNESS OF SEAMLESS COLD WORKED TUBEA,B
Nominal Outside Diameter, in. (mm)
Permissible Variations
Outside Diameter, in (mm)
Thickness of Specified Average Wall, %
Thickness of Specifined Minimum Wall, %
Plus
Minus
Plus
Minus
Plus
Minus
Over 0.400(10) to 5/8(16), excl
0.005(0.13)
0.005(0.13)
15.0
15.0
30
0
5/8(16) to 1 1/2(38), incl
0.075(0.19)
0.075(0.19)
10.0
10.0
22
0
Over 1 1/2(38) to 3 (76), incl
0.010(0.25)
0.010(0.25)
10.0
10.0
22
0
Over 3(76) to 4 1/2(114), incl
0.010(0.38)
0.010(0.38)
10.0
10.0
22
0
Over 4 1/2(114) to 6(152), incl
0.020(0.51)
0.020(0.51)
12.5
12.5
28
0
Over 6(162) to 6 5/8(168), incl
0.025(0.64)
0.025(0.64)
12.5
12.5
28
0
Over 6 5/8(168) to 8 5/8(219), incl
0.031(0.79)
0.031(0.79)
12.5
12.5
28
0
AOvality -The permissible variations in this table apply to individual measurements, incluluding out-of-roundness (ovality) except for the following: For pipe and tube having a nominal wall thickness of 3% or less of the nominal outside diameter, the mean outside diameter shall conform to the permissible variations of this table and individual measurements (including ovality) shall conform to the plus and minus values of the table, with the values increased by 0.5% of the nominal ouside diameter. For pipe and tube over 4 1/2 in. (114 mm) in outside diameter with a nominal wall thickness greater than 3% of the nominal ouside diameter with a nominal wall thickness greater than 3% of the nominal outside diameter, the mean outside diameter shall conform to the permissible variations of this table and individual measurements shall not exceed twice the permissible variations of the table. BEccentricity - The permissible variations in this table to individual measurements including eccentricity.
TABLE4 PERMISSIBLE VARIATIONS FOR OUTSIDE DIAMETER AND WALL THICKNESS OF SEAMLESS COLD-WORKED TUBEA,B
Nominal O utside Diameter in. (mm)
Permissible Variations
OutsideDiameter or Inside Diameter, in (mm)
% of Thickness of Specified Nominal Wall
% of Thickness of Specifined Minimum Wall,
Plus
Minus
Plus
Minus
Plus
Minus
3/4 (19) to 11/2(38), incl
0.015(0.4)
0.031(0.8)
12.5
12.5
28.5
0
Over 11/2(38.1) to 4(102), incl
0.031(0.8)
0.031(0.8)
12.5
12.5
28.5
0
Over 4(102) to 9 1/4(235), incl
0.062(1.6)
0.031(0.8)
12.5
12.5
28.5
0
AOvality - For tube 5 in. (127mm) and under in outside diameter, the tolerance on the outside diameter applies for individual measurements and includes ovality. For tube over 5 in. (125 mm) in outside diameter, the mean outside diameter shall conform to the permissible variations of this table and individual measurements shall not exceed twice the permissible variations of this table.
TABLE5 PERMISSIBLE VARIATIONS FOR OUTSIDE DIAMETER AND WALL THICKNESS OF SEAMLESS COLD-WORKED PIPEA,B
Nominal Outside Diameter, in. (mm)
Permissible Variations
Outside Diameter, in (mm)
Thickness of Specified Average Wall, %
Thickness of Specifined Minimum Wall, %
Plus
Minus
Plus
Minus
Plus
Minus
2 1/2 (64) to 4 1/2(114), incl
0.031(0.79)
0.031(0.79)
16.0
12.5
28.5
0
Over 4 1/2(114) to 6 1/2(165), incl
0.047(1.2)
0.047(1.2)
16.0
12.5
28.5
0
Over 6 1/2(165) to 9 1/4(235), incl
0.062(1.6)
0.062(1.6)
16.0
12.5
28.5
0
AOvality - For tube 5 in. (127mm) and under in outside diameter, the tolerance on the outside diameter applies for individual measurements and includes ovality. For tube over 5 in. (125 mm) in outside diameter, the mean outside diameter shall conform to the permissible variations of this table and individual measurements shall not exceed twice the permissible variations of this table. BEccentricity - The permissible variations in this table apply to individual measurements including eccentricity.
TABLE6 PERMISSIBLE VARIATIONS IN LENGTHA
Outside Diameter, in.(mm)
Length Tolerance, in. (mm)
Over
Under
Under 2 (50.8)
1/8 (3.2)
0
2 (50.8) and over
3/16 (4.8)
0
AThese permissible variations in length apply to pipe in straight lengths. They apply to cut lengths up to and including 24 ft (7.3m). For lengths over 24 ft, an additional over-tolerance of 1/8 in. (3.2 mm) for each 10 ft (3 m) or fraction there of shall be permitted up to a maximum additional over-tolerance of 1/2 in. (12.7 mm).